Table 1
The composition and thermal properties of the samples are listeda)
| ID | Composition | Tg (K) | Tp (K) | Ta (K), ta (h) | ∆Tp (K) |
| 1 | La80Al15Ni5 | – | 463 | 363, 4 | 8.5 |
| 2 | La75Al5Ni20 | – | 464 | 383, 4 | 8 |
| 3 | Al87Ni10Ce3 | – | 518 | 403, 4 | 7 |
| 4 | Y65Co35 | 624 | 703 | 533, 4 | 0 |
| 5 | La60Al20Ni20 | 473 | 632 | 403, 4 | 0 |
| 6 | La55Al15Ni30 | 487 | 597 | 403, 4 | 0 |
| 7 | La50Al20Ni30 | 523 | 623 | 433, 4 | 0 |
| 8 | La50Al10Ni40 | 508 | 570 | 413, 4 | 0 |
| 9 | La50Al30Cu20 | 518 | 658 | 393, 4 | 0 |
| 10 | Al86Ni10Sm4 | 603 | 636 | 461, 4 | 0 |
| 11 | Al86Co9Ce5 | 632 | 662 | 543, 4 | 0 |
| 12 | Ce55Ni20Al25 | 506 | 628 | 393, 4 | 0 |
| 13 | Ge2Sb2Te5 [33] | – | 433 | 388, 1 | 4 |
| 14 | GeSe [33] | 568 | 590 | 438, 1 | 0 |
a) Thermodynamic parameters of different MGs obtained by FSC at a heating rate of 400 K/s. Tg and Tp are the glass transition temperature and peak crystallization temperature of the as-cast sample, respectively. Ta and ta are the annealing temperature and annealing time, respectively. ∆Tp indicates the difference in peak crystallization temperature before and after annealing.
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.