Table 1
The materials, preparation method, thickness, VOC and power generated by TEG reported in recent literatures
| Materials | Preparation method | Thickness | VOC (cm−2) | Power (cm−2) | Year | Ref. |
| ZnO/Ag/ITO | Hydrothermal reaction | 0.5 mm | 5.8 mV | 6.283 × 10−7 nW | 2012 | [91] |
| poly (3,4-ethylenedioxythiophene)(PEDOT)-Cl | Vapor deposition | ‒ | 23 mV | 4.5 nW | 2019 | [92] |
| CNT/polydimethylsiloxane (PDMS) | Vacuum filtration deposition and 3D printing | 5 mm | 0.72 mV | 416.22 nW | 2021 | [97] |
| CNT/PEDOT | Wet spinning | 110 μm | 0.7 mV | 0.3 μW | 2022 | [98] |
| Bi2Te3/Sb2Te3 | Screen printing | 1 mm | 76 mV | 655 μW | 2023 | [93] |
| PEDOT/tellurium nanowire (Te-NWs) | Hydrothermal reaction | 1 mm | 25 mV | 3.5 nW | 2023 | [94] |
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.